M.L. International offers Low Carbon Grade High Tensile Steel Strapping. M.L International offers a wide range of packaging machinery and materials. The cold rolled Low Carbon Grade High Tensile Steel Strapping is treated with a special process that combines the fine surface and controls the physical properties. The Mechanical Properties of these strappings are that the tensile strength of the strapping is 70 - 85 Kgs/ square mm with 0 - 3 percent over 150 mm gauge length elongation per minute. The maximum proportion of chemical components in these strapping is Carbon [0.05 - 0.15 percent], Manganese [0.30 - 0.60 percent], Sulphur [0.05 percent], Phosphorus [0.05 percent] and Silicon [0.30 percent]. The sizes vary from 12.70 mm to 31.75 mm with thickness ranges from 0.38 mm to 1.27 mm, however special sizes can be manufactured. The width of the tolerances is +0.127mm and -0.127mm with +0.05mm and -0.025mm thickness around. The strapping is painted in Standard Brown / Black Colour / Zinc Color and the wax is lubricated for ideal corrosion resistance and also to improve the tension transmission around all corners of the package. The weight of the low carbon coil is 22 to 55 kgs with Ribbon wound sizes ranging from 31.75 mm to 19.05 mm in width and the Mill wound sizes ranges from 19.05 mm to 12.70 mm in width. The inner Diameter is 400 / 406 mm and the outer Diameter is 550 to 670 mm. The straightness is free, it is also in curl, chamber and twist in shape. The edges of the steel strapping are smooth debarred and rounded.