Product Profile of Vinyl Silane Grafted Low Density Polyethylene Compound
Vinyl Silane Grafted Low Density Polyethylene Compound is used in low voltage insulation and sheathing in power cables. The Low Density Polyethylene Compound can be extruded as a normal thermoplastic. GEM Polytech Industries Pvt. Ltd, an ISO 9001:2008 awarded company, manufactures Vinyl Silane Grafted Low Density Polyethylene Compound.
GEM Polytech Industries Pvt. Ltd supplies wide ranges of zero halogen low smoke compound, XLPE compound, thermoplastic semi conductive compound, silane grafted polyethylene compound, conductive compounds etc. The Vinyl Silane Grafted Low Density Polyethylene Compound can be used in aerial bunch cables with 5 - 6.25% carbon black master batch.
Vinyl Silane Grafted Low Density Polyethylene Compound has the following specifications:
- Density: 0.925 gm / cube cm.
- Tensile Strength at Break: 15 MPa.
- Elongation at break: 400%.
- Variation on tensile strength 168hrs/135 degree C: ± 15%.
- Variation on elongation at break 168hrs/135 degree C: ± 15%.
- Hot Set Elongation under load at 200 degree C, 0.2N/ sq mm:50%.
- Permanent Elongation after Cooling: ± 5 %.
- Power factor at 50 Hz at 23 degree C: 0.0004.
- Dielectric Constant: 2.3.
- Volume Resistively at 20 degree C: greater than X 10¹6 Ohm cm.
- Dielectric Strength: 25Kv/mm.
Product Specification of Vinyl Silane Grafted Low Density Polyethylene Compound
- Density:0.925 gm/cm³
- Dielectric Constant:2.3
- Dielectric Strength:25 Kv/mm
- Elongation at Break:400
- Power Factor:0.0004
- Tensile Strength:15
- Volume Resistivity:1x1016